| TEM Investigation on the Microstructural Evolution of Hastelloy N Induced by Ar+ Ion Irradiation | |
| Liu, M; Lu, YL; Liu, RD; Zhou, XT; liumin@sinap.ac.cn; zhouxingtai@sinap.ac.cn | |
| 2014 | |
| Source Publication | MICROSCOPY RESEARCH AND TECHNIQUE
 |
| ISSN | 1059-910X |
| Volume | 77Issue:2Pages:161—169 |
| Abstract | Hastelloy N alloy has been selected as the primary structure material for molten salt reactor. In this article, Hastelloy N alloy samples were irradiated to different doses at room temperature using 300 keV Ar+ ions. The microstructural evolution was investigated by transmission electron microscopy (TEM) and energy-dispersive spectroscopy (EDS). Black dot defects emerged in sample irradiated at low dose (0.4 displacement per atom (dpa)), and they grew up with irradiation doses (0.4-2 dpa). A high density of small dislocation loops (nano meters in size) were observed in the sample irradiated to 4 dpa. When the ion dose increased to 12 dpa, complicated structures with defects (including dislocation lines, larger loops and smaller black dots) were observed. Dislocation networks were detected from high-angle annular dark field (HAADF) images. Larger dislocation loops (size: 30-80 nm) were visible in the sample irradiated to 40 dpa. Irradiation with dose of 120 dpa led to the formation of face-centered cubic nanocrystallites with preferred orientations. Microsc. Res. Tech. 77:161-169, 2014. (c) 2013 Wiley Periodicals, Inc. |
| Keyword | Base Alloys Cu Alloys Temperature Corrosion Copper Damage Steel |
| Indexed By | SCI |
| Language | 英语 |
| WOS ID | WOS:000329879400008 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.sinap.ac.cn/handle/331007/14465 |
| Collection | 中科院上海应用物理研究所2011-2019年 |
| Corresponding Author | liumin@sinap.ac.cn; zhouxingtai@sinap.ac.cn |
| Recommended Citation GB/T 7714 | Liu, M,Lu, YL,Liu, RD,et al. TEM Investigation on the Microstructural Evolution of Hastelloy N Induced by Ar+ Ion Irradiation[J]. MICROSCOPY RESEARCH AND TECHNIQUE,2014,77(2):161—169. |
| APA | Liu, M,Lu, YL,Liu, RD,Zhou, XT,liumin@sinap.ac.cn,&zhouxingtai@sinap.ac.cn.(2014).TEM Investigation on the Microstructural Evolution of Hastelloy N Induced by Ar+ Ion Irradiation.MICROSCOPY RESEARCH AND TECHNIQUE,77(2),161—169. |
| MLA | Liu, M,et al."TEM Investigation on the Microstructural Evolution of Hastelloy N Induced by Ar+ Ion Irradiation".MICROSCOPY RESEARCH AND TECHNIQUE 77.2(2014):161—169. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| TEM Investigation on（1152KB） | 开放获取 | CC BY-NC-SA | View Download | |||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment