| Bio-inspired laminated graphite nanosheets/copper composites | |
| Wang, P; Liu, W; Chen, L; Mu, C; Qi, G; Bian, F | |
| 2015 | |
| Source Publication | RSC ADVANCES
 |
| Volume | 5Issue:63Pages:51342—51346 |
| Subtype | 期刊文献 |
| Abstract | As one of the most industrially important metals, copper (Cu) was successfully reinforced with graphite nanosheets (GNSs). A nacre-inspired laminated GNSs/Cu composite material was fabricated by a combination of ball-milling and hot-rolling techniques. During the ball-milling process, the GNSs were in situ produced from graphite exfoliation. The Cu-GNSs composite ingot was hot-rolled into a belt to form a laminated structure. The laminated Cu-GNSs composite material showed improved mechanical properties observed from tensile and three-point bending tests. The Young's modulus of Cu-GNSs composites was up to 170 GPa and the bending strength reached 660 MPa. This processing route was also advantageous in low-cost, mass-producing manufacture. |
| Keyword | Enhanced Mechanical-properties Biomimetic Nanolaminated Composites Graphene-copper Composites Flake Powder-metallurgy Matrix Composites Carbon Nanotubes Layer Graphene Nanocomposites Nacre Microstructure |
| Indexed By | SCI |
| Language | 英语 |
| Document Type | 期刊论文 |
| Identifier | http://ir.sinap.ac.cn/handle/331007/24403 |
| Collection | 中科院上海应用物理研究所2011-2020年 |
| Recommended Citation GB/T 7714 | Wang, P,Liu, W,Chen, L,et al. Bio-inspired laminated graphite nanosheets/copper composites[J]. RSC ADVANCES,2015,5(63):51342—51346. |
| APA | Wang, P,Liu, W,Chen, L,Mu, C,Qi, G,&Bian, F.(2015).Bio-inspired laminated graphite nanosheets/copper composites.RSC ADVANCES,5(63),51342—51346. |
| MLA | Wang, P,et al."Bio-inspired laminated graphite nanosheets/copper composites".RSC ADVANCES 5.63(2015):51342—51346. |
| Files in This Item: | ||||||
| File Name/Size | DocType | Version | Access | License | ||
| Bio-inspired laminat（641KB） | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | View Application Full Text | |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment