题名: In situ synchrotron small- and wide-angle X-ray study on the structural evolution of Kevlar fiber under uniaxial stretching
作者: Li, XY; Tian, F; Zhou, P; Yang, CM; Li, XH; Bian, FG; Wang, J
刊名: RSC ADVANCES
出版日期: 2016
卷号: 6, 期号:85, 页码:81552-81558
DOI: 10.1039/c6ra17671b
通讯作者: Yang, CM ; Li, XH (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai Synchrotron Radiat Facil, Shanghai, Peoples R China.
文章类型: 期刊论文
英文摘要: The structural evolution and mechanism of Kevlar 29 and Kevlar 129 (poly(p-phenylene terephthalamide)) fibers during stretching were studied by in situ synchrotron small-angle X-ray scattering (SAXS) and wide-angle X-ray scattering (WAXS). Compared with Kevlar 29, the tensile strength of Kevlar 129 increased, while the elongation-to-break ratio decreased. SAXS results showed that ordered lamellae were observed only in Kevlar 29. The fibril length of Kevlar 129 was larger than that of Kevlar 29; however, the fibril misorientation width of Kevlar 129 was smaller. During stretching, both the fibril length and fibril misorientation width decreased at low strains, and then increased until the fibrils broke both in Kevlar 29 and Kevlar 129 fibers. From WAXS results, the crystal orientation angle decreased in Kevlar 29 during stretching, while that in Kevlar 129 increased at low strains and then decreased until the fibers broke. The change of crystallinity indicated that the amorphous phase can convert to the crystal phase at high strains, although the conversion ratio was not large. By combining the SAXS and WAXS results, a potential mechanism for Kevlar fibers during stretching was proposed.
收录类别: SCI
语种: 英语
WOS记录号: WOS:000382776000013
ISSN号: 2046-2069
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.sinap.ac.cn/handle/331007/26538
Appears in Collections:中科院上海应用物理研究所2011-2017年_期刊论文

Files in This Item: Download All
File Name/ File Size Content Type Version Access License
In situ synchrotron small- and wide-angle X-ray study on the structural evolution of Kevlar fiber under uniaxial stretching.pdf(784KB)期刊论文作者接受稿开放获取View Download
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[Li, XY]'s Articles
[Tian, F]'s Articles
[Zhou, P]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[Li, XY]‘s Articles
[Tian, F]‘s Articles
[Zhou, P]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit
文件名: In situ synchrotron small- and wide-angle X-ray study on the structural evolution of Kevlar fiber under uniaxial stretching.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Powered by CSpace