题名: Intermediate temperature embrittlement of one new Ni-26W-6Cr based superalloy for molten salt reactors
作者: Jiang, L; Ye, XX; Cui, CY; Huang, HF; Leng, B; Li, ZJ; Zhou, XT
刊名: MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
出版日期: 2016
卷号: 668, 页码:137-145
关键词: Intermediate temperature embrittlement ; Dynamic recrystallization ; Ni-26W-6Cr ; Molten salt reactors
DOI: 10.1016/j.msea.2016.04.032
通讯作者: Li, ZJ (reprint author), Chinese Acad Sci, Shanghai Inst Appl Phys, Thorium Molten Salts Reactor Ctr, Shanghai 201800, Peoples R China.
文章类型: 期刊论文
英文摘要: Ni-26W-6Cr based superalloy is considered a potential structure material for the molten salt reactors due to its high strength and good compatibility with the fluoride salt. In the present work, the temperature dependence of the tensile behavior of the alloy was studied by tensile tests in the temperature range of 25-850 degrees C. This alloy exhibited a good ductility at RT and 450 degrees C, a ductility minimum from 650 to 750 degrees C and an intermediate ductility at 850 degrees C. TEM and EBSD characterization was performed on specimens tested at three typical temperature points (RT, 650 degrees C and 850 degrees C) to determine the deformation and fracture mechanisms accounting for the intermediate temperature embrittlement. At RT, the grain boundaries can accommodate enough dislocations to provide compatibility of the sliding between adjacent grains, then M6C carbides act as crack origins and cause the fracture. In case of 650 degrees C, the grain boundaries cannot withstand the local stress even if only a small number of dislocation pile-ups exist. The premature cracks at grain boundaries impede the development of plastic deformation from single slips to multiple ones and cause the low ductility. If tested at 850 degrees C, the fracture process is retarded by the dynamic recovery and local dynamic recrystallization at crack tips. (C) 2016 Elsevier B.V. All rights reserved.
收录类别: SCI
语种: 英语
WOS记录号: WOS:000378468500017
ISSN号: 0921-5093
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.sinap.ac.cn/handle/331007/26547
Appears in Collections:中科院上海应用物理研究所2011-2017年_期刊论文

Files in This Item: Download All
File Name/ File Size Content Type Version Access License
Intermediate temperature embrittlement of one new Ni-26W-6Cr based superalloy for molten salt reactors.pdf(3096KB)期刊论文作者接受稿开放获取View Download
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[Jiang, L]'s Articles
[Ye, XX]'s Articles
[Cui, CY]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[Jiang, L]‘s Articles
[Ye, XX]‘s Articles
[Cui, CY]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit
文件名: Intermediate temperature embrittlement of one new Ni-26W-6Cr based superalloy for molten salt reactors.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Powered by CSpace