题名:
Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process
作者: Yu, JC; Chen, K; Li, XY; Tian, F; Chen, SH; Zhang, YM; Wang, HP
刊名: JOURNAL OF APPLIED POLYMER SCIENCE
出版日期: 2016
卷号: 133, 期号:41, 页码:-
关键词: ageing ; fibers ; structure-property relations ; thermal properties
DOI: 10.1002/app.44078
通讯作者: Zhang, YM (reprint author), Donghua Univ, Coll Mat Sci & Engn, State Key Lab Modificat Chem Fibers & Polymer Mat, Shanghai 201620, Peoples R China.
文章类型: 期刊论文
英文摘要: The changes in performance during thermal-oxidative aging process of the aromatic co-polysulfonamide (co-PSA) fibers over a broad temperature range from 250 degrees C to 320 degrees C have been investigated. In addition, the mechanism of thermal-oxidative aging process has been studied by using structural information obtained from the fibers at varying length scales. The results showed that a significant reduction in tensile strength was observed compared with that of initial modulus during aging process. Macroscopically, thermal-oxidative aging mainly causes color changes of fibers and thermally induced macro defects begin to appear only at 320 degrees C for 100 h. On a micro level, the crystal structure of fibers remained stable and did not show significant changes expect that aging at 320 degrees C. In addition, thermo-degradation as well as crosslinking has been observed primarily in amorphous region. With the increase of temperature and time duration, the crosslinking became more dominant and crosslinking density increases. Correspondingly, the fibril length decreases due to degradation and then increases due to the formation of crosslinked structures within the fibers. The results suggest that molecular degradation is the main cause of strength loss and the formation of crosslinking structure within the fibers contributes to the retention of modulus and improvement of creep resistance. (C) 2016 Wiley Periodicals, Inc.
收录类别: SCI
语种: 英语
WOS记录号: WOS:000380728200013
ISSN号: 0021-8995
Citation statistics:
内容类型: 期刊论文
URI标识: http://ir.sinap.ac.cn/handle/331007/26595
Appears in Collections:中科院上海应用物理研究所2011-2017年_期刊论文

Files in This Item: Download All
File Name/ File Size Content Type Version Access License
Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process.pdf(1153KB)期刊论文作者接受稿开放获取View Download

Recommended Citation:
Yu, JC,Chen, K,Li, XY,et al. Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process[J]. JOURNAL OF APPLIED POLYMER SCIENCE,2016-01-01,133(41):-.
Service
Recommend this item
Sava as my favorate item
Show this item's statistics
Export Endnote File
Google Scholar
Similar articles in Google Scholar
[Yu, JC]'s Articles
[Chen, K]'s Articles
[Li, XY]'s Articles
CSDL cross search
Similar articles in CSDL Cross Search
[Yu, JC]‘s Articles
[Chen, K]‘s Articles
[Li, XY]‘s Articles
Related Copyright Policies
Null
Social Bookmarking
Add to CiteULike Add to Connotea Add to Del.icio.us Add to Digg Add to Reddit
文件名: Performance and structure changes of the aromatic co-polysulfonamide fibers during thermal-oxidative aging process.pdf
格式: Adobe PDF
所有评论 (0)
暂无评论
 
评注功能仅针对注册用户开放,请您登录
您对该条目有什么异议,请填写以下表单,管理员会尽快联系您。
内 容:
Email:  *
单位:
验证码:   刷新
您在IR的使用过程中有什么好的想法或者建议可以反馈给我们。
标 题:
 *
内 容:
Email:  *
验证码:   刷新

Items in IR are protected by copyright, with all rights reserved, unless otherwise indicated.

 

 

Valid XHTML 1.0!
Powered by CSpace