Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt
Zhu, HL; Holmes, R; Hanley, T; Davis, J; Short, K; Edwards, L; Li, ZJ
2017
Source PublicationCORROSION SCIENCE
ISSN0010-938X
Volume125Issue:-Pages:184-193
Subtype期刊论文
AbstractSamples of a Ni-Mo-Cr-Fe-Si alloy subject to helium ion irradiation damage were corroded in a eutectic mixture of FLiNaK at 750 degrees C. It was found that the helium bubbles that formed increased the number of surface defects so greatly increasing the physical contact area between the alloy and the molten salt, resulting in acceleration of corrosion damage. Segregation and depletion of chemical elements at bubble surfaces were also identified, and became more severe with increasing bubble size. Significant segregation of Si resulted in the formation of Ni-Si precipitates at large bubbles. This segregation enhanced the chemical corrosion damage to the alloy.
KeywordRadiation-induced Segregation Behavior Nickel Diffusion Metals Kinetics
DOI10.1016/j.corsci.2017.06.027
WOS KeywordRADIATION-INDUCED SEGREGATION ; BEHAVIOR ; NICKEL ; DIFFUSION ; METALS ; KINETICS
Indexed BySCI
Language英语
WOS IDWOS:000407535500018
Citation statistics
Cited Times:5[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.sinap.ac.cn/handle/331007/28632
Collection中科院上海应用物理研究所2011-2018年
Recommended Citation
GB/T 7714
Zhu, HL,Holmes, R,Hanley, T,et al. Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt[J]. CORROSION SCIENCE,2017,125(-):184-193.
APA Zhu, HL.,Holmes, R.,Hanley, T.,Davis, J.,Short, K.,...&Li, ZJ.(2017).Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt.CORROSION SCIENCE,125(-),184-193.
MLA Zhu, HL,et al."Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt".CORROSION SCIENCE 125.-(2017):184-193.
Files in This Item: Download All
File Name/Size DocType Version Access License
Effects of bubbles o(4343KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Zhu, HL]'s Articles
[Holmes, R]'s Articles
[Hanley, T]'s Articles
Baidu academic
Similar articles in Baidu academic
[Zhu, HL]'s Articles
[Holmes, R]'s Articles
[Hanley, T]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Zhu, HL]'s Articles
[Holmes, R]'s Articles
[Hanley, T]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Effects of bubbles on high-temperature corrosion of helium ion-irradiated Ni-based alloy in fluoride molten salt.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.