Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests
Zhou, BJ; Wang, LY; Chen, B; Jia, YW; Wen, W; Li, DJ; Shu, D; Jin, PP; Zeng, XQ; Ding, WJ
2017
发表期刊MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING
ISSN0921-5093
卷号708期号:-页码:319-328
文章类型期刊论文
摘要Microstructure evolution of a supersaturated solid solution Mg-2.2 wt%Nd alloy during aging at 240 degrees C for 6 h (stage I), at 295 degrees C for 3 h (stage II), and finally at 320 degrees C for 1 h (stage III) was studied by in situ synchrotron X-Ray diffraction. In stage I, diffraction from beta(1) (Mg3Nd, FCC) precipitates was observed after similar to 15 min. Evolution of the volume, size, and aspect ratio of beta(1) with the aging time were estimated from peak intensity and peak width analysis. In stage II, diffraction from beta (Mg12Nd, tetragonal) precipitates was observed after similar to 36 min while beta(1) remained in the material. In stage III, the volume of h reduced substantially in relative to beta. The identified precipitation sequence from the in situ aging experiment is supported by ex situ electron microscopy observations. beta', which had not been detected by synchrotron X-rays, was additionally found using transmission electron microscopy in the material by the end of aging stage I. Tension and hardness tests using specimens with different aging conditions were further performed to understand how different precipitates affect the strength and ductility of the Mg-Nd alloy.
关键词Mg-re Alloys Magnesium Alloys Precipitate Morphology Phase Microstructure Fabrication Simulation Evolution
DOI10.1016/j.msea.2017.10.011
关键词[WOS]MG-RE ALLOYS ; MAGNESIUM ALLOYS ; PRECIPITATE MORPHOLOGY ; PHASE ; MICROSTRUCTURE ; FABRICATION ; SIMULATION ; EVOLUTION
收录类别SCI
语种英语
WOS记录号WOS:000415770100033
引用统计
文献类型期刊论文
条目标识符http://ir.sinap.ac.cn/handle/331007/28835
专题中科院上海应用物理研究所2011-2018年
推荐引用方式
GB/T 7714
Zhou, BJ,Wang, LY,Chen, B,et al. Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests[J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,2017,708(-):319-328.
APA Zhou, BJ.,Wang, LY.,Chen, B.,Jia, YW.,Wen, W.,...&Ding, WJ.(2017).Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests.MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING,708(-),319-328.
MLA Zhou, BJ,et al."Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests".MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING 708.-(2017):319-328.
条目包含的文件 下载所有文件
文件名称/大小 文献类型 版本类型 开放类型 使用许可
Study of age hardeni(2411KB)期刊论文作者接受稿开放获取CC BY-NC-SA浏览 下载
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Zhou, BJ]的文章
[Wang, LY]的文章
[Chen, B]的文章
百度学术
百度学术中相似的文章
[Zhou, BJ]的文章
[Wang, LY]的文章
[Chen, B]的文章
必应学术
必应学术中相似的文章
[Zhou, BJ]的文章
[Wang, LY]的文章
[Chen, B]的文章
相关权益政策
暂无数据
收藏/分享
文件名: Study of age hardening in a Mg-2.2 wt%Nd alloy by in situ synchrotron X-ray diffraction and mechanical tests.pdf
格式: Adobe PDF
此文件暂不支持浏览
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。