| Effects of the phase interface on spallation damage nucleation and evolution in multiphase alloy | |
| Yang, Y; Wang, C; Chen, XZ; Hu, HB; Chen, KG; Fu, YN | |
| 2018 | |
| Source Publication | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| ISSN | 0925-8388 |
| Volume | 740Pages:321-329 |
| Subtype | 期刊论文 |
| Abstract | The spall behaviors of Cu-34%Zn-3%Pb leaded brass samples with annealing and cryogenic treating conditions were dynamic loaded using one-stage light gas gun experiments under similar to 1.515 GPa shock pressure. The effects of alpha/beta phase interface and Pb/matrix phase interface on dynamic damage nucleation, growth, and coalescence in leaded brass specimens were investigated by multidimensional testing techniques. Experiment results showed that voids of incipient spall were mainly nucleated in the interior of the Pb-phases with signs of melting, and a small number of voids were nucleated in alpha-phase, and both are not nucleated at the interface which contradicts the damage fracture theory under quasi-static loading. Due to the effect of reflection and transmission of shock wave at the phase interface, when the shock wave propagates from alpha-phase with higher impedance to Pb-phase or beta-phase with lower impedance, a tensile pulse will be formed within alpha-phase. If the tensile pulse has sufficient amplitude voids would be nucleated in alpha-phase. On the other hand, it is considered that the asymmetry high compression zones in the center of the lead-phase with low impedance were formed by the shock wave convergence effects of matrix/lead quasi-spherical interface, which caused adiabatic temperature rise exceeded melting point of lead due to severe plastic deformation, and finally led to local melting and void nucleation in the center of the lead-phase rather than the tensile stress. (C) 2018 Elsevier B.V. All rights reserved. |
| Keyword | High-purity Copper Sweeping Detonation Behavior Failure Metals Cu |
| DOI | 10.1016/j.jallcom.2018.01.031 |
| Indexed By | SCI |
| Language | 英语 |
| WOS ID | WOS:000425494200039 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://ir.sinap.ac.cn/handle/331007/28987 |
| Collection | 中科院上海应用物理研究所2011-2018年 |
| Affiliation | 1.Yang, Y 2.Wang, C 3.Chen, XZ 4.Hu, HB 5.Chen, KG 6.Fu, YN |
| Recommended Citation GB/T 7714 | Yang, Y,Wang, C,Chen, XZ,et al. Effects of the phase interface on spallation damage nucleation and evolution in multiphase alloy[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2018,740:321-329. |
| APA | Yang, Y,Wang, C,Chen, XZ,Hu, HB,Chen, KG,&Fu, YN.(2018).Effects of the phase interface on spallation damage nucleation and evolution in multiphase alloy.JOURNAL OF ALLOYS AND COMPOUNDS,740,321-329. |
| MLA | Yang, Y,et al."Effects of the phase interface on spallation damage nucleation and evolution in multiphase alloy".JOURNAL OF ALLOYS AND COMPOUNDS 740(2018):321-329. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| Effects of the phase（3850KB） | 期刊论文 | 作者接受稿 | 开放获取 | CC BY-NC-SA | View Download | |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment