Transformation of metallic polymer precursor into nanosized HfTaC2 ceramics
Sun, YN; Yang, CM; Lu, Y; Chen, FH; Han, WJ; Qiu, WF; Ye, L; Li, XH; Zhao, T
2020
Source PublicationCERAMICS INTERNATIONAL
ISSN0272-8842
Volume46Issue:5Pages:6022-6028
Subtype期刊论文
AbstractPolymeric precursor for HfTaC2 ceramic was prepared by coordination reaction between metal alkoxides and acetylacetone, subsequent hydrolysis, and blend with oligomeric novolac carbon sources. The phase analysis and microstructure study were conducted using X-ray diffraction (XRD), scanning electron microscope (SEM) and transmission electron microscopy (TEM). It showed that after pyrolyzed at 1450 degrees C for 90 min, HfTaC2 was obtained with particle size similar to 50 nm and uniform elemental distribution. Phase transition from precursor to ceramic was studied by in situ XRD measurements at temperatures from 800 to 1200 degrees C. In the early stage, oxide solid solution Hf6Ta2O17 was firstly detected at similar to 950 degrees C, followed by Ta2O5 and TaO. As temperature was raised, signals for TaO and Hf6Ta2O17 gradually weakened and disappeared, while those for other phases strongly strengthened. Furthermore, formation of HfxTayCz solid solution was monitored and confirmed by peak migration during 1300 degrees C isothermal treatment. When the sample was pyrolyzed at 1450 degrees C, solid solution HfxTayCz was detected at different holding time. Phase structure at 90 min was the closest to standard HfTaC2 with particle size D-v (90) similar to 200 nm.
KeywordHAFNIUM CARBIDE MICROSTRUCTURE ZIRCONIUM SILICON TAC BEHAVIOR TA4HFC5 HFC
DOI10.1016/j.ceramint.2019.11.059
Indexed BySCI ; EI
Language英语
Citation statistics
Cited Times:3[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://ir.sinap.ac.cn/handle/331007/33218
Collection中科院上海应用物理研究所2011-2020年
Affiliation1.Chinese Acad Sci, Inst Chem, Beijing 100190, Peoples R China
2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China
3.Chinese Acad Sci, Shanghai Inst Appl Phys, Shanghai Synchrotron Radiat Facil, Shanghai 201204, Peoples R China
4.South China Univ Technol, South China Adv Inst Soft Sci & Technol, Guangzhou 510640, Peoples R China
Recommended Citation
GB/T 7714
Sun, YN,Yang, CM,Lu, Y,et al. Transformation of metallic polymer precursor into nanosized HfTaC2 ceramics[J]. CERAMICS INTERNATIONAL,2020,46(5):6022-6028.
APA Sun, YN.,Yang, CM.,Lu, Y.,Chen, FH.,Han, WJ.,...&Zhao, T.(2020).Transformation of metallic polymer precursor into nanosized HfTaC2 ceramics.CERAMICS INTERNATIONAL,46(5),6022-6028.
MLA Sun, YN,et al."Transformation of metallic polymer precursor into nanosized HfTaC2 ceramics".CERAMICS INTERNATIONAL 46.5(2020):6022-6028.
Files in This Item: Download All
File Name/Size DocType Version Access License
Transformation of me(2418KB)期刊论文出版稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Sun, YN]'s Articles
[Yang, CM]'s Articles
[Lu, Y]'s Articles
Baidu academic
Similar articles in Baidu academic
[Sun, YN]'s Articles
[Yang, CM]'s Articles
[Lu, Y]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Sun, YN]'s Articles
[Yang, CM]'s Articles
[Lu, Y]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Transformation of metallic polymer precursor into nanosized HfTaC2 ceramics.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.